06 Jun 2017 Co2+:MgAl2O4 (or Co:Spinel) is a relatively new material for saturable absorber passive Q-switching in lasers emitting from 1.2 to 1.6 microns, in particular, for eye-safe 1.54 μm Er:glass laser.High absorption cross section of 3.5 x 10-19 cm2 permits Q-switching of Er:glass laser.High absorption cross section of 3.5 x 10-19 cm2 permits Q-switching of Er:glass laser without intracavity focusing both with flash lamp and diode-laser pumping. Negligible excited-state absorption results in high contrast of Q-switch, i.e. the ratio of initial (small signal) to saturated absorption is higher than 10.
|
Characteristics of Spinel Crystal
|
|
crystals structure
|
cubic
|
|
Spatial group
|
Fd3m
|
|
Element ary cell parameters,
|
0.8086nm
|
|
Thermal Conductivity
|
17W/m.k @20deg.
|
|
Thermal Expansion
|
7.33x10-6/k
|
|
Modulus of elasticity
|
2.3x 10^5
|
|
Density,
|
3.58g/cm 3
|
|
Mohs hardness
|
8
|
|
Melting point,
|
2105 ° C
|
|
Refraction index
|
1.6.-1.75
|
|
|
486.1nm
|
1.72433
|
|
546.1nm
|
1.71976
|
|
589.3nm
|
1.71611
|
|
656.3nm
|
1.71268
|
Working wavelength range, 1.2 – 1.6μm
Absorption cross-section, 3.5×10-19 (at 1.54 μm)cm2
Specifications:
|
T0
|
From 30% to 98% 1540nm
|
|
Dimension tolerance
|
(W ± 0.1 mm) x (H ± 0.1 mm)
|
|
Transmitting wavefront distortion:
|
L/8 @ 633 nm
|
|
Clear aperture:
|
> 90% central area
|
|
Flatness:
|
L/8 @ 633 nm
|
|
Scratch/Dig code:
|
10/5 to MIL-O-13830A
|
|
Parallelism:
|
better than 20 arc seconds
|
|
Perpendicularity:
|
5 arc minutes
|
|
Angle tolerance:
|
Dq < ±0.5°, Df < ± 0.5°
|
|
AR coating:
|
R< 0.2% at 1540nm
|
|
Quality Warranty Period:
|
one year under proper use.
|
Note: When ordering Co:MgAl2O4 crystal, please specify the aperture, initial transmission(To) and coatings. |